第48卷第2期2020年2月
聚氯乙烯
辐射取暖器Polyvinyl Chloride
Vol.48,No.2
李荣顺*，赖萍，蒋华庭
(华之杰塑料建材有限公司，浙江德清313200)七巧板的制作方法
［摘要］在PVC型材覆膜之前，通常采用清洗剂来去除脱模剂以提高其表面张力，但清洗剂会污染环境。为了解决此问题，进行了机械抛光试验，考察了其提高PVC型材表面张力的效果。结果表明：采用软毛刷进行逆向抛光，当压入深度为5〜10nun时，可使PVC型材的表面张力达到覆膜的要求。
［中图分类号］TQ325.3［文献标志码］B［文章编号］1009-7937(2020)02-0025-03
Study on improving surface tension of PVC profiles
LI Rongshun,LAI Ping,JfANG Huating
(Huazhijie Plastic Building Material Co.,Ltd.,Deqing313200,China)
Key words:PVC profile；film lamination；surface tension；brush
Abstract:Eefbre PVC profiles were laminated w让h film,cleaning agent was usually used to remove the release agent to improve the surface tension,but the cleaning agent will pollute the environment.In order to solve this problem,mechanical polishing test was carried out.The effects of the test on improving the surface tension of PVC profiles were investigated.The results showed that the surface tension of PVC profiles could meet the requirements of film lamination when the surface was polished with the soft-brush in the reverse direction and the pressed depth was5—10mm.
PVC型材的表面彩化，目前主要有表面共挤(ASA.PMMA等)、表面氟碳喷涂/滚涂、表面覆膜、表面转印后光固化等工艺，其中国内主要的加工工艺为ASA表面共挤，其次为表面氟碳喷涂和表面覆膜，表面转印后光固化工艺主要用于吊顶制品和墙面装饰制品。但因表面共挤、氟碳喷涂型材在后期应用时存在不足(主要表现为日照弯曲、变脆等)，目前欧美发达国家还是以表面覆膜型材为主。在表面覆
膜的工序中，由于刚挤出的PVC型材表面有一层脱模剂(主要是外润滑剂)，型材的表面张力较低，难以达到38dyn/cm(编者注：dyn即达因，在表征表面张力时常用的单位，1dyn=10-5N)的最低要求，无法与胶黏剂有效粘接，因此目前普遍采用酮类或苯类清洗剂进行覆膜前的清洗。作为易挥发的有机溶剂，酮类或苯类清洗剂对环境存在污染，因此部分发达国家已禁止此类清洗剂的生产，随着我国环保力度的加大，将来也有禁止的可能。因此，开发新的提高PVC型材表面张力的方法很有必要。
1提高PVC型材表面张力的方法
除清洗剂表面清洗法外，还有下面3种提高PVC型材表面张力的方法。
(1)电晕-等离子处理法，在高压电场下对PVC型材表面进行电晕放电，产生低温等离子体，增加PVC型材表面粗糙度和表面积。该方法的缺点是规模化生产投资大，且PVC型材处理后表面张力随时间衰减明显，个别产品需要进行二次处理。
(2)等离子化学沉降法，通过在PVC型材表面涂覆一层无机-有机聚合物来提高表面张力，但其余热制冷
.［收稿日期］2019-11-20
连通区域［作者简介］李荣顺(1967—)，男，正高级工程师，毕业于吉林工学院高分子材料专业，多年从事高分子材料合成与加工方面的工作，获得多项国家级、省部级奖项，发表论文4篇，申请专利4项，现任
前继华之杰塑料建材有限公司总工程师。
25