2020年第48卷第4期DOI ：10.13588/j. cnki. g. e. 2096-7608. 2020. 04.008浮法薄玻璃下表面划伤及锡印质量缺陷分析与改进 **收稿日期:2020-04-01唐文鹏
（成都南玻玻璃有限公司，四川成都610200）雕刻笔
按摩毯
摘要：分析了浮法薄玻璃下表面划伤和锡印的产生机理，揭示了渣箱及附近区域特殊的温度场，以及玻璃带 与辐道之间相对速差，提出了超薄玻璃下表面划伤和锡印的预防措施，对相关结构设计提出了改进建议。关键词：薄玻璃；划伤；锡印；硬度；相对速差木醋
中图分类号：TQ171.6+5 文献标志码：B 文章编号：2096-7608（2020）04-0033-06
The Analysis of Scratch and Tin Smear Problems on the Bottom Surface of Float Glass and Their Solutions
TANG Wenpeng
(Chengdu CSG Glass CO. , LTD. , Chengdu 610200, China)猎结构
显示器电路板Abstract : The analysis of the causes of the scratch and tin smear on the bottom surface of thin float glass was carried out ； the specific temperature field in the dross box and the surrounding area, and the relative velocity difference between the glass ribbon and the rollers were revealed. The prevention measures from scratches and tin smears on the bottom surface of ultra — thin float glass were put forward and the im provement for the related structural design was proposed.
Key words : thin glass ； scratch ； tin smear ； hardness , relative velocity difference
o 引言
浮法薄玻璃和超薄玻璃的重要用途之一是生产电子设备的显示器件，其表面质量直接影响显示器件的 外观和使用性能，已成为（超）薄玻璃生产中极为重要的质量指标。相关标准E 对划伤和表面污渍有严格要 求：1）规格406 mmX356 mm 的玻璃，允许宽度为0.03-0.07 mm 的划伤总长度不超过5 mm/片，宽度大 于0. 07 mm 的划伤不允许有（实际使用时要求更为严格）；2）表面污渍不允许有。搜 同
为了改善下表面质量，提升产品整体质量水平和成品率，研究人员对超薄玻璃生产线进行了大量攻关工 作，但生产中仍时常受到划伤和污渍的困扰；同时，浮法薄玻璃对下表面质量的要求已与超薄玻璃基本一致, 但并未得到足够重视和研究。因此，本文将针对划伤与下表面锡印展开讨论。