Designation: D 3359 – 02
名称： D 3359-02
Standard Test Methods for
Measuring Adhesion by Tape Test1
ASTM D3359-09 标准试验方法 扩阴器
胶带法测量附着力 This standard is issued under the fixed designation D 3359; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
这个标准是D 3359确定了以后发行的。数字代表名称最初通过的时间，或者修订情况，和最新版本。括号内的数字代表最新重新审批时间。上标代表最新版本的变化或重新审批。
This standard has been approved for use by agencies of the Department of Defense.
该标准已经被国防机构部门批准使用。
1. Scope 范围
1.1 These test methods cover procedures for assessing the adhesion of coating films to metallic substrates by applying and removing pressure-sensitive tape over cuts made in the film.
本标准提出的试验方法是规定通过在漆膜切割区施加和撕离压敏胶带的方式，对漆膜与金属底材之间的附 着力进行评定的程序 1.2 Test Method A is primarily intended for use at job sites while Test Method B is more suitable for use in the laboratory. Also, Test Method B is not considered suitable for films thicker than 5 mils (125µ直流调压器m).
试验方法A主要是供工作场所用，而试验方法B更适合实验室使用。试验方法B被视为不适合厚度超过 5毫英寸（125微米）的漆膜。
NOTE 1—Subject to agreement between the purchaser and the seller,Test Method B can be used for thicker films if wider spaced cuts are employed.
注 1-根据买卖双方的协议，如果切割间距较宽，漆膜较厚时可采用试验方法B。
1.3 These test methods are used to establish whether the adhesion of a coating to a substrate is at a generally adequate level. They do not distinguish between higher levels of adhesion for which more sophisticated methods of measurement are required.
本标准规定的试验方法用于总体判定涂层与底材之间的附着力是否达到足够的水平。如果附着力较高，本标准规定的试验方法无法精确地区分附着力的差别，需要使用更精确的测量方法。 NOTE 2—It should be recognized that differences in adherability of the coating surface can affect the results obtained with coatings having the same inherent adhesion.
注2-应该注意到，涂层内在附着力相同的情况下，涂覆面附着性的差别会影响测量结果。
1.4 In multicoat systems adhesion failure may occur between coats so that the adhesion of the coating system to the substrate is not determined.
多层涂层体系可能出现层间脱落，无法确定涂层体系与底材之间的附着力。
1.5 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
SI单位的数值被视为标准，括号内的数值仅供参考.
1.6 This standard does not purport to address the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
本标准并没有指出与其使用相关的所有安全事项。本标准的用户应负责在使用之前采取适当的安全和卫生 措施，并确定各项管理限制条件的适用性
2. Referenced Documents 参考文件
2.1 ASTM Standards: 美国材料与试验协会标准
D 609 Practice for Preparation of Cold-Rolled Steel Panels for Testing Paint, Varnish, Conversion Coatings, and Related Coating Products2
D609-涂料,清漆,转化涂层和相关覆层产品的测试-用冷轧钢板制备的标准实施规范
D 823 Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels2
D823-漆,清漆,喷漆及有关产品制成厚度均匀漆膜试片的方法
D 1000 Test Method For Pressure-Sensitive Adhesive-Coated Tapes Used for Electrical and Electronic Applications3聚氨酯生产工艺
D1000-电气设备用压合敏感胶粘剂涂覆带的试验方法
D 1730 Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting4
D1730- 涂漆用铝和铝合金表面预处理标准实施规范
D 2092 Guide for Preparation of Zinc-Coated (Galvanized) Steel Surfaces for Painting5
D2092-用于涂漆的镀锌钢材表面预处理的标准指南
D 2370 Test Method for Tensile Properties of Organic Coatings2
D2370-有机涂层抗拉性能的标准试验方法。
D 3330 Test Method for Peel Adhesion of Pressure-Sensitive Tape 6
D3330- 导热油配方压敏胶带剥离强度测试标准
电梯应急装置D 3924 Specification for Standard Environment for Conditioning and Testing Paint, Varnish, Lacquer, and Related Materials2
D 3924-漆,清漆,喷漆和相关物质状态调节和试验用标准环境规范
D 4060 Test Method for Abrasion Resistance of Organic Coatings by the Taber Abraser2
D 4060 -用泰伯尔磨蚀机测定有机涂层耐磨性的标准试验方法
3. Summary of Test Methods 试验方法摘要
3.1 Test Method A—An X-cut is made through the film to the substrate, pressure-sensitive tape is applied over the cut and then removed, and adhesion is assessed qualitatively on the 0 to 5 scale.
试验方法A：一个抗干扰滤波器X切口贯通漆膜和底材 ，在切口处施加和移除压敏胶带，粘附力按照0-5等级进行评估。
3.2 Test Method B—A lattice pattern with either six or eleven cuts in each direction is made in the film to the substrate, pressure-sensitive tape is applied over the lattice and